PA12
UnfilledUnfilled nylon: tough, wear-resistant and good under repeated loading. Dried before printing because it absorbs moisture.
Best for Gears and bushings · Living hinges · Wear parts
Material Guide
Nylon
Polyamide (PA6 / PA12)
Best for high-wear mechanical parts, living hinges, and parts under repeated load.
Typical accuracy±0.2–0.4 mm
Nozzle240–270 °C
Bed70–90 °C
Glass transition~50–60 °C
Heat deflection~80–100 °C
Introduction
What Nylon is and when to use it
Nylon (polyamide, most commonly PA6 or PA12 in FDM printing) is the material to reach for when a part needs to survive thousands of load cycles, resist abrasion, or flex repeatedly without cracking — the kind of duty cycle that would fatigue PLA, PETG, or even ABS. It's the closest thing on this list to a true engineering thermoplastic, used in gears, living hinges, tool handles, and load-bearing brackets in production far beyond 3D printing.
That performance comes with real process demands. Nylon is intensely hygroscopic — it pulls moisture from the air fast enough that a spool left unsealed for even a few hours can print noticeably worse, with popping, poor layer bonding, and rough surface finish as the absorbed moisture flashes to steam at the nozzle. It also shrinks more than PETG or PLA as it cools, and it doesn't bond well to a bare glass or PEI bed without a specific adhesion aid. None of this makes nylon hard to print so much as it makes nylon unforgiving of shortcuts — dry filament and a stable, warm bed aren't optional the way they might be for PLA.
In practice, this makes nylon the right choice at IMECA3D whenever a part needs genuine mechanical durability over time — gears, hinges, snap-fits that get used repeatedly, or brackets under continuous vibration — and the wrong choice whenever a faster or more forgiving material would do the job just as well.
Grades we print
Nylon (PA) types and when to use each
Every grade below can be printed on our Bambu Lab printers. Not sure which one fits? Describe the part and we'll recommend one.
PA6-CF
Carbon fibreCarbon-fibre filled PA6: very stiff and strong, with high heat resistance.
Best for Structural brackets · Tooling and fixtures · Parts near heat sources
- Heat resistance
- Impact resistance
- Tensile strength
PA6-GF
Glass fibreGlass-fibre filled PA6: strong, stiff and dimensionally stable.
Best for Structural parts · Housings under load · Fixtures
- Heat resistance
- Impact resistance
- Tensile strength
PAHT-CF
High temperatureHigh-temperature nylon with carbon fibre. It absorbs less moisture than PA6 grades, so its properties stay more stable in humid conditions.
Best for Engine-bay and hot-zone parts · End-use functional parts · Stiff structural parts
- Heat resistance
- Impact resistance
- Tensile strength
Performance Profile
Key material characteristics
Tolerances
Dimensional accuracy & clearances
Typical accuracy±0.2–0.4 mm, more variable than PETG or ABS depending on filament dryness
Nylon's shrinkage and moisture sensitivity make it the least dimensionally predictable material straight off the printer — but it's also the most forgiving once assembled, since its ductility lets a slightly tight fit "break in" through use rather than crack outright the way PLA would. Expect to iterate on clearance more than with other materials, especially across different humidity conditions.
* Nylon's flexibility often allows tighter working hinges than the table suggests. Living hinges are a special case: nylon is one of the few FDM materials that can survive a thin, repeatedly flexed hinge section without fatigue cracking, provided the hinge is printed with continuous perimeters running along the flex axis rather than across it.
Recommended clearances
Press fit0.20–0.30 mm
Sliding fit0.30–0.45 mm
Hinged mechanism*0.35–0.55 mm
Rotating assembly0.40–0.60 mm
Loose fit0.55–0.80 mm
00.250.500.751.00 mm
Thermal Limits
Thermal properties
0 °C306090120 °C
Heat deflection (HDT) Glass transition (Tg) Hot car interior, 65–70 °C
| Property | Value |
|---|---|
| Glass transition temperature (Tg) | ~50–60 °C (varies by grade) |
| Heat deflection temperature (HDT) | ~80–100 °C (PA6/PA12 blends, varies by formulation) |
Nylon's heat performance depends heavily on which grade you're using — PA12 tends to have better dimensional stability and lower moisture uptake, while PA6 generally offers higher strength and heat resistance at the cost of being even more moisture-sensitive. For most functional prototyping we specify a PA12-based or nylon-composite blend for its better print behavior; for parts where higher heat resistance matters more than ease of printing, a PA6 formulation may be worth the added process discipline.
Recommended Parameters
Recommended print settings
Nozzle temperature
240–270 °C
Bed temperature
70–90 °C
Print speed
30–45 mm/s
Cooling
Low
Similar to PETG — excess cooling weakens layer bonding
Layer height
0.2 mm standard
Finer layers for gear teeth or precision features
Bed adhesion
Adhesion aid (glue stick, specialty bed surface, or nylon-specific adhesive) strongly recommended
Filament drying
Dry before every print
4–8 h at ~70 °C, stored in a sealed container with desiccant between prints
Drying isn't a one-time step — nylon reabsorbs moisture from ambient air within hours of leaving a sealed container, so the practical workflow is dry-then-print, not dry-once. If a print shows popping sounds, rough or fuzzy surface texture, or weak layer adhesion, moisture is the first thing to check before adjusting anything else.
Engineering Guidance
Design guidelines for engineers
01
Wall thickness
3+ perimeters for load-bearing parts, though nylon's toughness means thinner walls fail more gracefully here than they would in PLA — useful for parts where some flex is acceptable or even desired.
02
Infill
25–40% for gears, brackets, and other parts under repeated mechanical load. For living hinges and other flex features, keep the flexing section as solid perimeters rather than infill, since infill patterns don't hold up well under repeated bending.
03
Layer orientation
Orient gear teeth, snap-fit tabs, and other small load-bearing features so the load path runs in-plane rather than across layers — nylon's inter-layer bond is good, but its in-plane strength and fatigue resistance are still meaningfully better.
04
Fastener features
Nylon is one of the few FDM materials well suited to printing its own threads directly, thanks to its wear resistance — though heat-set inserts are still the more durable option for parts that will be assembled and disassembled repeatedly.
05
Bed adhesion and warping
Because nylon shrinks unevenly on cooling, large flat parts benefit from the same design habits as ABS — avoid unbroken flat areas near the bed where possible, add a brim, and expect an enclosure to meaningfully improve results on anything larger than a small bracket.
Use Cases
Where Nylon fits in a project
Nylon earns its place wherever a part needs to survive real mechanical duty over time rather than a single load event. Typical uses at IMECA3D include:
- Gears, cams, and other wear components
- Living hinges and repeatedly flexed features
- Tool handles and grips
- Brackets and mounts under continuous vibration or cyclic load
- Functional end-use parts where fatigue life matters more than print speed or cost
When to move to a different material
If the part is a visual or fit-check prototype, PLA is faster, cheaper, and far more forgiving to print. If it needs good toughness and moisture resistance without nylon's drying requirements, PETG is the easier choice. If it needs heat resistance and solvent-based post-processing more than fatigue life, ABS is more practical. The impact resistance comparison and the filament comparison walk through those trade-offs.
Compare with
PLA
Fast, cheap and forgiving for visual and fit-check prototypes.
PETGToughness and moisture resistance without nylon's drying routine.
ABSHeat resistance and solvent-based post-processing.
Summary
Nylon is the material that asks the most of the printing process and gives the most back in return — genuine fatigue resistance, wear resistance, and toughness that none of the other common FDM filaments can match. Get the drying and bed adhesion right, and nylon parts will outlast almost anything else under real mechanical duty. Skip the drying step, and it's the one material where a shortcut shows up immediately in the print.